ABS granules Medium impact resistance 100% virgin

Physical property table of ABS PA-757 Granules

Basic Information  

E56070-565071

RoHS compliance

RoHS compliance

processing methods

injection molding

Physical Property of ABS PA-757 Granules

Rating   Unit    Test Method

Specific gravity

    -- 1.05 g/cm³ ASTM D792

    23°C 1.05 g/cm³ ISO 1183

Melt flow rate (melt flow rate) ASTM D1238

    200°C/5.0kg 1.6g/10min ASTM D1238

    220°C/10.0 kg 22 g/10 min ASTM D1238

Melted Volume Flow Rate (MVR) (220°C/10.0 kg) 22.0 cm³/10min ISO 1133

Hardness Rating Unit Test Method

Rockwell hardness (R scale) 116 ASTM D785

Ball hardness (H 358/30) 110 MPa ISO 2039-1

Mechanical Property of ABS PA-757 Granules

Rating   Unit   Test Method

tensile stress

    Yield 54.0 MPa ISO 527-2/50

    Break 37.0 MPa ISO 527-2/50

    3.00 mm 1 45.1 MPa ASTM D638

Elongation      

    Break, 3.00 mm 2 25 % ASTM D638

    Break 20 % ISO 527-2/50

Flexural modulus

    6.00 mm 3 2650 MPa ASTM D790

    -- 4 2200 MPa ISO 178

Bending strength      

    6.00 mm 5 77.5 MPa ASTM D790

-- 6 76.0 MPa ISO 178

Impact Performance of ABS PA-757 Granules

Rating   Unit    Test Method

Charpy notched impact strength 20 kJ/m² ISO 179

Simply supported beam unnotched impact strength without fracture ISO 179

Notched Izod Impact Strength

    23°C, 3.00 mm 210 J/m ASTM D256

    23°C, 6.00 mm 180 J/m ASTM D256

    -- 18 kJ/m² ISO 180/1A

Unnotched Izod impact strength 60 kJ/m² ISO 180/1U

Thermal Peformance of ABS PA-757 Granules

Rating    Unit    Test Method

    1.8 MPa, unannealed 85.0 °C ASTM D648

    1.8 MPa, unannealed 88.0 °C ISO 75-2/A

    1.8 MPa, Annealed 95.0 °C ASTM D648

    1.8 MPa, Annealed 98.0 °C ISO 75-2/A

Vicat softening temperature

    -- 105 °C ASTM D1525 7

    -- 104 °C ISO 306/A50

-- 100 °C ISO 306/B50

Flammability performance of ABS PA-757 Granules

Rating    Test    Method

UL flame rating (1.60 mm) HB UL 94

Injection Performance of ABS PA-757 Granules

Rating Unit System

Drying temperature 80.0 to 85.0 °C

Drying time 2.0 to 4.0 hr

Back of barrel temperature 180 to 220 °C

Mid barrel temperature 190 to 230 °C

Front barrel temperature 190 to 230 °C

Mold temperature 30.0 to 70.0 °C

Remark

1.6.0 mm/min

2.6.0 mm/min

3.2.8 mm/min

4.2.0mm/min

5.2.8 mm/min

6.2.0 mm/min

7 . Rate A (50°C/h)